Search for: All records

Epitaxial multilayer heterostructures of ScxAl1−xN/GaN with Sc contents x = 0.11–0.45 are found to exhibit significant differences in structural quality, chemical impurity levels, and electronic properties depending on the starting Sc source impurity levels. A higher purity source leads to a 2–3 orders of magnitude reduction in the carbon, oxygen, and fluorine unintentional doping densities in MBE-grown ScxAl1−xN/GaN multilayers. Electrical measurements of ScxAl1−xN/n+GaN single heterostructure barriers show a 5–7 orders of magnitude reduction in the electrical leakage for films grown with a higher purity Sc source at most Sc contents. The measured chemical and electrical properties of epitaxial ScxAl1−xN highlight the importance of the starting Sc source material purity for epitaxial device applications that need these highly piezoelectric and/or ferroelectric transition-metal nitride alloys. 

Conductive homoepitaxial Si-doped β-Ga2O3 films were fabricated by pulsed laser deposition with an as-deposited 2323 S cm−1 conductivity (resistivity = 4.3 × 10−4 Ω-cm, carrier concentration = 2.24 × 1020 cm−3, mobility = 64.5 cm2 V−1 s−1, and electrical activation efficiency = 77%). High quality homoepitaxial films deposited on commercial (010) Fe-compensated β-Ga2O substrates were determined by high-resolution transmission electron microscopy and x-ray diffraction. The β-Ga2O3 films have ∼70% transparency from 3.7 eV (335 nm) to 0.56 eV (2214 nm). The combination of high conductivity and transparency offers promise for numerous ultrawide bandgap electronics and optoelectronic applications. 

β-Ga2O3 is a promising ultra-wide bandgap semiconductor whose properties can be further enhanced by alloying with Al. Here, using atomic-resolution scanning transmission electron microscopy, we find the thermodynamically unstable γ-phase is a ubiquitous structural defect in both β-(AlxGa1−x)2O3 films and doped β-Ga2O3 films grown by molecular beam epitaxy. For undoped β-(AlxGa1−x)2O3 films, we observe γ-phase inclusions between nucleating islands of the β-phase at lower growth temperatures (∼500–600 °C). In doped β-Ga2O3, a thin layer of the γ-phase is observed on the surfaces of films grown with a wide range of n-type dopants and dopant concentrations. The thickness of the γ-phase layer was most strongly correlated with the growth temperature, peaking at about 600 °C. Ga interstitials are observed in the β-phase, especially near the interface with the γ-phase. By imaging the same region of the surface of a Sn-doped β-(AlxGa1−x)2O3 after ex situ heating up to 400 °C, a γ-phase region is observed to grow above the initial surface, accompanied by a decrease in Ga interstitials in the β-phase. This suggests that the diffusion of Ga interstitials toward the surface is likely the mechanism for growth of the surface γ-phase and more generally that the more-open γ-phase may offer diffusion pathways to be a kinetically favored and early forming phase in the growth of Ga2O3. However, more modeling and simulation of the γ-phase and the interstitials are needed to understand the energetics and kinetics, the impact on electronic properties, and how to control them. 

We report the in situ, direct epitaxial synthesis of (0001)-oriented PdCoO2 thin films on c-plane sapphire using ozone-assisted molecular-beam epitaxy. The resulting films have smoothness, structural perfection, and electrical characteristics that rival the best in situ grown PdCoO2 thin films in the literature. Metallic conductivity is observed in PdCoO2 films as thin as ∼2.0 nm. The PdCoO2 films contain 180° in-plane rotation twins. Scanning transmission electron microscopy reveals that the growth of PdCoO2 on the (0001) surface of Al2O3 begins with the CoO2 layer.